Material 1.0425

High-temperature constructional steel

1.0425 is pressure-vessel steeel grade. Its tensile strength is between 410 and max. 530 N/mm².This grade is weldable. 1.0425 is being used for steam boilers as well as pressurized vessel constructions.

Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.

1.0425

Standards

HDIN / EN US-Standard AFNOR UNI JIS request
P265GH H2 ASTM A515Grade60 ASTM A516Grade60 Fe4101KW Fe4101KG Fe4101KT Fe4102KW Fe4102KG SG295 SGV410 SGV450 SGV480 SPV315 SPV355 request

Material Category: High-temperature constructional steel

Chemical Composition

C % Si % Mn % P % S % Al % Cr % Cu % Mo % N % Nb % Ni % Ti % V %
max 0,20 max 0,40 0,80 - 1,40 max 0,025 max 0,010 min 0,0200 max 0,30 max 0,30 max 0,08 max 0,012 max 0,020 max 0,30 max 0,03 max 0,02

 

Mechanical Properties

DIN EN 10028-2
Flacherzeugnisse aus Druckbehälterstählen. Unlegierte und legierte Stähle mit festgelegten Eigenschaften bei erhöhten Temperaturen.
normalgeglüht Streckgrenze (Re) Zugfestigkeit (Rm)  Bruchdehnung (A5,65) Kerbschlagarbeit KV2 (ISO-V/Charpy-V)
<= 16 mm >= 265 N/mm² 410 - 530 N/mm² >= 22 % >= 27 Joule ~ -20 ° C
<= 16 mm       >= 34 Joule ~ 0 ° C
16 - 40 mm >= 255 N/mm² 410 - 530 N/mm² >= 22 % >= 40 Joule ~ 20 ° C
16 - 40 mm       >= 27 Joule ~ -20 ° C
40 - 60 mm >= 245 N/mm² 410 - 530 N/mm² >= 22 % >= 34 Joule ~ 0 ° C
40 - 60 mm       >= 40 Joule ~ 20 ° C
60 - 100 mm >= 215 N/mm² 410 - 530 N/mm² >= 22 % >= 27 Joule ~ -20 ° C
60 - 100 mm       >= 34 Joule ~ 0 ° C
100 - 150 mm >= 200 N/mm² 400 - 530 N/mm² >= 22 % >= 40 Joule ~ 20 ° C
100 - 150 mm       >= 27 Joule ~ -20 ° C
150 - 250 mm >= 185 N/mm² 390 - 530 N/mm² >= 22 % >= 34 Joule ~ 0 ° C
150 - 250 mm       >= 40 Joule ~ 20 ° C
 
0,2% Dehngrenze (Rp0,2) Wert bei Temperatur
<= 16 mm  >= 256 N/mm² ~ 50 ° C      
<= 16 mm >= 241 N/mm² ~ 100 ° C      
<= 16 mm >= 223 N/mm² ~ 150 ° C      
<= 16 mm >= 205 N/mm² ~ 200 ° C      
<= 16 mm >= 188 N/mm² ~ 250 ° C      
<= 16 mm >= 173 N/mm² ~ 300 ° C      
<= 16 mm >= 160 N/mm² ~ 350 ° C      
<= 16 mm >= 150 N/mm² ~ 400 ° C      
16 - 40 mm >= 247 N/mm² ~ 50 ° C      
16 - 40 mm >= 232 N/mm² ~ 100 ° C      
16 - 40 mm >= 215 N/mm² ~ 150 ° C      
16 - 40 mm >= 197 N/mm² ~ 200 ° C      
16 - 40 mm >= 181 N/mm² ~ 250 ° C      
16 - 40 mm >= 166 N/mm² ~ 300 ° C      
16 - 40 mm >= 154 N/mm² ~ 350 ° C      
16 - 40 mm >= 145 N/mm² ~ 400 ° C      
40 - 60 mm >= 237 N/mm² ~ 50 ° C      
40 - 60 mm >= 223 N/mm² ~ 100 ° C      
40 - 60 mm >= 206 N/mm² ~ 150 ° C      
40 - 60 mm >= 190 N/mm² ~ 200 ° C      
40 - 60 mm >= 174 N/mm² ~ 250 ° C      
40 - 60 mm >= 160 N/mm² ~ 300 ° C      
40 - 60 mm >= 148 N/mm² ~ 350 ° C      
40 - 60 mm >= 139 N/mm² ~ 400 ° C      
60 - 100 mm >= 208 N/mm² ~ 50 ° C      
60 - 100 mm >= 196 N/mm² ~ 100 ° C      
60 - 100 mm >= 181 N/mm² ~ 150 ° C      
60 - 100 mm >= 167 N/mm² ~ 200 ° C      
60 - 100 mm >= 153 N/mm² ~ 250 ° C      
60 - 100 mm >= 140 N/mm² ~ 300 ° C      
60 - 100 mm >= 130 N/mm² ~ 350 ° C      
60 - 100 mm >= 122 N/mm² ~ 400 ° C      
100 - 150 mm >= 193 N/mm² ~ 50 ° C      
100 - 150 mm >= 182 N/mm² ~ 100 ° C      
100 - 150 mm >= 169 N/mm² ~ 150 ° C      
100 - 150 mm >= 155 N/mm² ~ 200 ° C      
100 - 150 mm >= 142 N/mm² ~ 250 ° C      
100 - 150 mm >= 130 N/mm² ~ 300 ° C      
100 - 150 mm >= 121 N/mm² ~ 350 ° C      
100 - 150 mm >= 114 N/mm² ~ 400 ° C      
150 - 250 mm >= 179 N/mm² ~ 50 ° C      
150 - 250 mm >= 168 N/mm² ~ 100 ° C      
150 - 250 mm >= 156 N/mm² ~ 150 ° C      
150 - 250 mm >= 143 N/mm² ~ 200 ° C      
150 - 250 mm >= 131 N/mm² ~ 250 ° C      
150 - 250 mm >= 121 N/mm² ~ 300 ° C      
150 - 250 mm >= 112 N/mm² ~ 350 ° C      
150 - 250 mm >= 105 N/mm² ~ 400 ° C      
DIN EN 10028-2
Flacherzeugnisse aus Druckbehälterstählen. Unlegierte und legierte Stähle mit festgelegten Eigenschaften bei erhöhten Temperaturen.
Zeitdehngrenze 10.000 h (Rp 1,0) Zeitdehngrenze 100.000 h (Rp 1,0) Zeitstandfestigkeit 10.000 h Zeitstandfestigkeit 100.000 h Zeitstandfestigkeit 200.000 h
Wert bei Temperatur Wert bei Temperatur Wert bei Temperatur Wert bei Temperatur Wert bei Temperatur
~ 164 N/mm² ~ 380 °C ~ 118 N/mm² ~ 380 °C ~ 229 N/mm² ~ 380 °C ~ 165 N/mm² ~ 380 °C ~ 145 N/mm² ~ 380 °C
~ 150 N/mm² ~ 390 °C ~ 106 N/mm² ~ 390 °C ~ 211 N/mm² ~ 390 °C ~ 148 N/mm² ~ 390 °C ~ 129 N/mm² ~ 390 °C
~ 136 N/mm² ~ 400 °C ~ 95 N/mm² ~ 400 °C ~ 191 N/mm² ~ 400 °C ~ 132 N/mm² ~ 400 °C ~ 115 N/mm² ~ 400 °C
~ 124 N/mm² ~ 410 °C ~ 84 N/mm² ~ 410 °C ~ 174 N/mm² ~ 410 °C ~ 118 N/mm² ~ 410 °C ~ 101 N/mm² ~ 410 °C
~ 113 N/mm² ~ 420 °C ~ 73 N/mm² ~ 420 °C ~ 158 N/mm² ~ 420 °C ~ 103 N/mm² ~ 420 °C ~ 89 N/mm² ~ 420 °C
~ 101 N/mm² ~ 430 °C ~ 65 N/mm² ~ 430 °C ~ 142 N/mm² ~ 430 °C ~ 91 N/mm² ~ 430 °C ~ 78 N/mm² ~ 430 °C
~ 91 N/mm² ~ 440 °C ~ 57 N/mm² ~ 440 °C ~ 127 N/mm² ~ 440 °C ~ 79 N/mm² ~ 440 °C ~ 67 N/mm² ~ 440 °C
~ 80 N/mm² ~ 450 °C ~ 49 N/mm² ~ 450 °C ~ 113 N/mm² ~ 450 °C ~ 69 N/mm² ~ 450 °C ~ 57 N/mm² ~ 450 °C
~ 72 N/mm² ~ 460 °C ~ 42 N/mm² ~ 460 °C ~ 100 N/mm² ~ 460 °C ~ 59 N/mm² ~ 460 °C ~ 48 N/mm² ~ 460 °C
~ 62 N/mm² ~ 470 °C ~ 35 N/mm² ~ 470 °C ~ 86 N/mm² ~ 470 °C ~ 50 N/mm² ~ 470 °C ~ 40N/mm² ~ 470 °C
~ 53 N/mm² ~ 480 °C ~ 30 N/mm² ~ 480 °C ~ 75 N/mm² ~ 480 °C ~ 42 N/mm² ~ 480 °C ~ 33 N/mm² ~ 480 °C

Back to the overview and search.

Material request

Screenreader label 
K3J_________29J______
N_F____6______4___ER7
F8P___2JI_____5______
N_1____P______E___GGK
M4M___________3______
* mandatory field
Screenreader label

Company

Five reasons that are in favor of BASEDO STEEL

Learn more

Services

A short overview of our services

Learn more

Questions?

Would you like to ask us about your specific demands?

Contact us