Material 1.0473

High-temperature constructional steel

1.0473 is a pressure-vessel steel grade. Its tensile strength is between 510 and max. 650 N/mm².This grade is well weldable. 1.0473 is being used for steam boilers as well as pressurized vessel constructions.

Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.

1.0473

Standards

HDIN / EN US-Standard AFNOR UNI JIS request
P355GH 19Mn6 UNS K02700 UNS K02803 UNS K FeE355-2 SGV410 SGV450 SGV480 SPV355 request

Material Category: High-temperature constructional steel

Chemical Composition

C % Si % Mn % P % S % Al % Cr % Cu % Mo % N % Nb % Ni % Ti % V %
0,10 - 0,22 max 0,60 1,00 - 1,70 max 0,025 max 0,010 min 0,0200 max 0,30 max 0,30 max 0,08 max 0,012 max 0,030 max 0,30 max 0,03 max 0,02

 

Mechanical Properties

DIN EN 10028-2
Flacherzeugnisse aus Druckbehälterstählen. Unlegierte und legierte Stähle mit festgelegten Eigenschaften bei erhöhten Temperaturen.
normalgeglüht Streckgrenze (Re) Zugfestigkeit (Rm)  Bruchdehnung (A5,65) Kerbschlagarbeit KV2 (ISO-V/Charpy-V)
<= 16 mm >= 355 N/mm² 510 - 650 N/mm² >= 20 % >= 27 Joule ~ -20 ° C
<= 16 mm       >= 34 Joule ~ 0 ° C
16 - 40 mm >= 345 N/mm² 510 - 650 N/mm² >= 20 % >= 40 Joule ~ 20 ° C
16 - 40 mm       >= 27 Joule ~ -20 ° C
40 - 60 mm >= 335 N/mm² 510 - 650 N/mm² >= 20 % >= 34 Joule ~ 0 ° C
40 - 60 mm       >= 40 Joule ~ 20 ° C
60 - 100 mm >= 315 N/mm² 490 - 630 N/mm² >= 20 % >= 27 Joule ~ -20 ° C
60 - 100 mm       >= 34 Joule ~ 0 ° C
100 - 150 mm >= 295 N/mm² 490 - 630 N/mm² >= 20 % >= 40 Joule ~ 20 ° C
100 - 150 mm       >= 27 Joule ~ -20 ° C
150 - 250 mm >= 280 N/mm² 490 - 630 N/mm² >= 20 % >= 34 Joule ~ 0 ° C
150 - 250 mm       >= 40 Joule ~ 20 ° C
 
0,2% Dehngrenze (Rp0,2) Wert bei Temperatur
<= 16 mm >= 343 N/mm² ~ 50 ° C      
<= 16 mm >= 323 N/mm² ~ 100 ° C      
<= 16 mm >= 299 N/mm² ~ 150 ° C      
<= 16 mm >= 275 N/mm² ~ 200 ° C      
<= 16 mm >= 252 N/mm² ~ 250 ° C      
<= 16 mm >= 232 N/mm² ~ 300 ° C      
<= 16 mm >= 214 N/mm² ~ 350 ° C      
<= 16 mm >= 202 N/mm² ~ 400 ° C      
16 - 40 mm >= 334 N/mm² ~ 50 ° C      
16 - 40 mm >= 314 N/mm² ~ 100 ° C      
16 - 40 mm >= 291 N/mm² ~ 150 ° C      
16 - 40 mm >= 267 N/mm² ~ 200 ° C      
16 - 40 mm >= 245 N/mm² ~ 250 ° C      
16 - 40 mm >= 225 N/mm² ~ 300 ° C      
16 - 40 mm >= 208 N/mm² ~ 350 ° C      
16 - 40 mm >= 196 N/mm² ~ 400 ° C      
40 - 60 mm >= 324 N/mm² ~ 50 ° C      
40 - 60 mm >= 305 N/mm² ~ 100 ° C      
40 - 60 mm >= 282 N/mm² ~ 150 ° C      
40 - 60 mm >= 259 N/mm² ~ 200 ° C      
40 - 60 mm >= 238 N/mm² ~ 250 ° C      
40 - 60 mm >= 219 N/mm² ~ 300 ° C      
40 - 60 mm >= 202 N/mm² ~ 350 ° C      
40 - 60 mm >= 190 N/mm² ~ 400 ° C      
60 - 100 mm >= 305 N/mm² ~ 50 ° C      
60 - 100 mm >= 287 N/mm² ~ 100 ° C      
60 - 100 mm >= 265 N/mm² ~ 150 ° C      
60 - 100 mm >= 244 N/mm² ~ 200 ° C      
60 - 100 mm >= 224 N/mm² ~ 250 ° C      
60 - 100 mm >= 206 N/mm² ~ 300 ° C      
60 - 100 mm >= 190 N/mm² ~ 350 ° C      
60 - 100 mm >= 179 N/mm² ~ 400 ° C      
100 - 150 mm >= 285 N/mm² ~ 50 ° C      
100 - 150 mm >= 268 N/mm² ~ 100 ° C      
100 - 150 mm >= 249 N/mm² ~ 150 ° C      
100 - 150 mm >= 228 N/mm² ~ 200 ° C      
100 - 150 mm >= 209 N/mm² ~ 250 ° C      
100 - 150 mm >= 192 N/mm² ~ 300 ° C      
100 - 150 mm >= 178 N/mm² ~ 350 ° C      
100 - 150 mm >= 167 N/mm² ~ 400 ° C      
150 - 250 mm >= 271 N/mm² ~ 50 ° C      
150 - 250 mm >= 255 N/mm² ~ 100 ° C      
150 - 250 mm >= 236 N/mm² ~ 150 ° C      
150 - 250 mm >= 217 N/mm² ~ 200 ° C      
150 - 250 mm >= 199 N/mm² ~ 250 ° C      
150 - 250 mm >= 183 N/mm² ~ 300 ° C      
150 - 250 mm >= 169 N/mm² ~ 350 ° C      
150 - 250 mm >= 159 N/mm² ~ 400 ° C      
DIN EN 10028-2
Flacherzeugnisse aus Druckbehälterstählen. Unlegierte und legierte Stähle mit festgelegten Eigenschaften bei erhöhten Temperaturen.
Zeitdehngrenze 10.000 h (Rp 1,0) Zeitdehngrenze 100.000 h (Rp 1,0) Zeitstandfestigkeit 10.000 h Zeitstandfestigkeit 100.000 h Zeitstandfestigkeit 200.000 h
Wert bei Temperatur Wert bei Temperatur Wert bei Temperatur Wert bei Temperatur Wert bei Temperatur
~ 195 N/mm² ~ 380 °C ~ 153 N/mm² ~ 380 °C ~ 291 N/mm² ~ 380 °C ~ 227 N/mm² ~ 380 °C ~ 206 N/mm² ~ 380 °C
~ 182 N/mm² ~ 390 °C ~ 137 N/mm² ~ 390 °C ~ 266 N/mm² ~ 390 °C ~ 203 N/mm² ~ 390 °C ~ 181 N/mm² ~ 390 °C
~ 167 N/mm² ~ 400 °C ~ 118 N/mm² ~ 400 °C ~ 243 N/mm² ~ 400 °C ~ 179 N/mm² ~ 400 °C ~ 157 N/mm² ~ 400 °C
~ 150 N/mm² ~ 410 °C ~ 105 N/mm² ~ 410 °C ~ 221 N/mm² ~ 410 °C ~ 157 N/mm² ~ 410 °C ~ 135 N/mm² ~ 410 °C
~ 135 N/mm² ~ 420 °C ~ 92 N/mm² ~ 420 °C ~ 200 N/mm² ~ 420 °C ~ 136 N/mm² ~ 420 °C ~ 115 N/mm² ~ 420 °C
~ 120 N/mm² ~ 430 °C ~ 80 N/mm² ~ 430 °C ~ 180 N/mm² ~ 430 °C ~ 117 N/mm² ~ 430 °C ~ 97 N/mm² ~ 430 °C
~ 107 N/mm² ~ 440 °C ~ 69 N/mm² ~ 440 °C ~ 161 N/mm² ~ 440 °C ~ 100 N/mm² ~ 440 °C ~ 82 N/mm² ~ 440 °C
~ 93 N/mm² ~ 450 °C ~ 59 N/mm² ~ 450 °C ~ 143 N/mm² ~ 450 °C ~ 85 N/mm² ~ 450 °C ~ 70 N/mm² ~ 450 °C
~ 83 N/mm² ~ 460 °C ~ 51 N/mm² ~ 460 °C ~ 126 N/mm² ~ 460 °C ~ 73 N/mm² ~ 460 °C ~ 60 N/mm² ~ 460 °C
~ 71 N/mm² ~ 470 °C ~ 44 N/mm² ~ 470 °C ~ 110 N/mm² ~ 470 °C ~ 63 N/mm² ~ 470 °C ~ 52 N/mm² ~ 470 °C
~ 63 N/mm² ~ 480 °C ~ 38 N/mm² ~ 480 °C ~ 96 N/mm² ~ 480 °C ~ 55 N/mm² ~ 480 °C ~ 44 N/mm² ~ 480 °C
~ 55 N/mm² ~ 490 °C ~ 33 N/mm² ~ 490 °C ~ 84 N/mm² ~ 490 °C ~ 47 N/mm² ~ 490 °C ~ 37 N/mm² ~ 490 °C
~ 49 N/mm² ~ 500 °C ~ 29 N/mm² ~ 500 °C ~ 74 N/mm² ~ 500 °C ~ 41 N/mm² ~ 500 °C ~ 30 N/mm² ~ 500 °C

Back to the overview and search.

Material request

Screenreader label 
HXO_________5NA______
__Z____F____D_1___UPW
9WI___MIW___IY8______
W______D______Z___MBB
LJ1_________JB3______
* mandatory field
Screenreader label

Company

Five reasons that are in favor of BASEDO STEEL

Learn more

Services

A short overview of our services

Learn more

Questions?

Would you like to ask us about your specific demands?

Contact us