Material 1.2357
Acero para herramientas de trabajo en caliente
El acero para herramientas 1.2357 tiene alta resistencia, buena resistencia al desgaste y resistencia a la compresión y puede pulirse bien. Con frecuencia, este material se utiliza para fabricar tijeras para chatarra.
Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.
Standards
| HDIN / EN | US-Standard | AFNOR | UNI | JIS | request |
|---|---|---|---|---|---|
| 50CrMoV13-14 | request |
Material Category: Acero para herramientas de trabajo en caliente
Chemical Composition
| C % | Si % | Mn % | P % | S % | Cr % | Mo % | V % |
| 0,45 - 0,55 | 0,20 - 0,50 | 0,25 - 0,50 | max 0,030 | max 0,030 | 3,00 - 3,60 | 1,20 - 1,60 | 0,05 - 0,25 |
Mechanical Properties
| geglüht | Härte (HB 30) | <= 248 HB 30 |
| gehärtet | Härte (HRC) | ~ 56 HRC |
| angelassen bei ~ 400 ° C | Härte (HRC) | ~ 53 HRC |
| angelassen bei ~ 450 ° C | Härte (HRC) | ~ 52 HRC |
| angelassen bei ~ 500 ° C | Härte (HRC) | ~ 51 HRC |
| angelassen bei ~ 550 ° C | Härte (HRC) | ~ 49 HRC |
| angelassen bei ~ 600 ° C | Härte (HRC) | ~ 47 HRC |