Material 1.4006
Acero inoxidable
El grado 1.4006 es un acero inoxidable martensítico. 1.4006 es muy popular para la construcción, es decir, plantas hidroeléctricas, ya que es resistente a la corrosión y tiene buenas propiedades mecánicas.
Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.
Standards
| HDIN / EN | US-Standard | AFNOR | UNI | JIS | request |
|---|---|---|---|---|---|
| X12Cr13 X10Cr13 | AISI 410 AISI 410mod UNS S41000 UNS S41001 | X12Cr13KG X12Cr13KW | SUS410 SUS410FB SUS410TB SUS410TKA SUS410TKC SUSF410-A SUSF410-B SUSF410-C SUSF410-D SUSY410 | request |
Material Category: Acero inoxidable
Chemical Composition
| C % | Si % | Mn % | P % | S % | Cr % | Ni % |
| 0,08 - 0,15 | max 1,00 | max 1,50 | max 0,040 | max 0,015 | 11,50 - 13,50 | max 0,75 |
Mechanical Properties
| geglüht | 0,2% Dehngrenze (Rp0,2) bei Temperatur | Zugfestigkeit (Rm) | Härte [HB 30] |
| >= 235 N/mm² ~ 100 ° C | <= 730 MPa | <= 220 HB 30 | |
| >= 230 N/mm² / ~ 150 ° C | |||
| >= 225 N/mm² / ~ 200 ° C | |||
| >= 225 N/mm² / ~ 250 ° C | |||
| >= 220 N/mm² / ~ 300 ° C | |||
| >= 210 N/mm² / ~ 350 ° C | |||
| >= 195 N/mm² / ~ 400 ° C |
| gehärtet | Zugfestigkeit (Rm) | Härte [HB 30] | Härte [HRC] |
| ~ 1.030 N/mm² | ~ 305 HB 30 | ~ 31 HRC |
| vergütet | 0,2% Dehngrenze (Rp0,2) bei Temperatur | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Einschnürung (Z) | Kerbschlagarbeit KV (ISO-V/Charpy-V) | Probenlage |
| >= 235 N/mm² ~ 100 ° C | ||||||
| >= 230 N/mm² / ~ 150 ° C | ||||||
| >= 225 N/mm² / ~ 200 ° C | ||||||
| >= 225 N/mm² / ~ 250 ° C | ||||||
| >= 220 N/mm² / ~ 300 ° C | ||||||
| >= 210 N/mm² / ~ 350 ° C | ||||||
| <= 160 mm | >= 195 N/mm² / ~ 400 ° C | 650 - 850 N/mm² | >= 15 % | >= 55 % | >= 25 Joule | längs |
| angelassen bei 680 - 780 ° C | Zugfestigkeit (Rm) |
| 650 - 850 N/mm² |