Material 1.4713

Heat-resisting steel

The material 1.4713 is a heat-resistant steel. This material is resistant to scaling up to a maximum temperature of about 800 °C / 1472 °F. 1.4713 is also known under the name Sicromal 8. 1.4713 is widely used in furnace construction.

Do you have any questions about the material or would you like to order? Complete our inquiry form, it`s free of charge and without obligation. We will get in touch with you in order to provide you with more information.

1.4713

Standards

HDIN / EN US-Standard AFNOR UNI JIS request
request

Material Category: Heat-resisting steel

Chemical Composition

C % Si % Mn % P % S % Al % Cr %
max 0,12 0,50 - 1,00 max 1,00 max 0,040 max 0,015 0,5000 - 1,0000 6,00 - 8,00

 

Mechanical Properties

DIN EN 10095 (12/2018 (05/1999))
Hitzebeständige Stähle und Nickellegierungen.
geglüht
Zeitdehngrenze 1.000 h (Rp 1,0) Zeitdehngrenze 10.000 h (Rp 1,0) Zeitdehngrenze 1.000 h Zeitdehngrenze 10.000 h Zeitdehngrenze 100.000 h bei Temperatur
~ 80 N/mm² ~ 50 N/mm² ~ 160 N/mm² ~ 100 N/mm² ~ 55 N/mm² ~ 500 ° C
~ 27,5 N/mm² ~ 17,5 N/mm² ~ 55 N/mm² ~ 35 N/mm² ~ 20 N/mm² ~ 600 ° C
~ 8,5 N/mm² ~ 4,7 N/mm² ~ 17 N/mm² ~ 9,5 N/mm² ~ 5 N/mm² ~ 700 ° C
~ 3,7 N/mm² ~ 2,1 N/mm² ~ 7,5 N/mm² ~ 4,3 N/mm² ~ 2,3 N/mm² ~ 800 ° C
~ 1,8 N/mm² ~ 1 N/mm² ~ 3,6 N/mm² ~ 1,9 N/mm² ~ 1 N/mm² ~ 900 ° C
Flacherzeugnisse
geglüht 0,2% Dehngrenze (Rp0,2) Zugfestigkeit (Rm) Bruchdehnung (A5, 65) Härte [HB] bei Temperatur
<= 12 mm >= 220 MPa 420 - 620 MPa   <= 192 HB ~ 20 ° C
>= 3 mm     >= 20 %   ~ 20 ° C
>= 3 mm     >= 15 %   ~ 20 ° C
Langerzeugnisse
geglüht Bruchdehnung (A5, 65) bei Temperatur
<= 12 mm >= 20 % ~ 20 ° C

Material request

Screenreader label
P79_________YQL______
__7____Y______C___JR7
FKQ___GQ9___9IL______
__I____6____6_____ZF7
EEP_________W6Z______
* mandatory field
Screenreader label

Company

Five reasons that are in favor of BASEDO STEEL

Learn more

Services

A short overview of our services

Learn more

Questions?

Would you like to ask us about your specific demands?

Contact us