Malzeme 1.3813
Non-magnetizable steel
The material 1.3813 is more rust and acid resistant.1.3813 is an amagnetic material. Often 1.3813 is supplied in hot cold worked condition. In this treatment condition, 1.3813 has a tensile strength at room temperature of 830 - 1030 N/mm² and a yield strength of at least 390 N/mm².
The density is approx. 7.9 kg/dm³.
The specific electrical resistance is approx. 0.7 (Ohm mm²)/m at a temperature of approx. 20 C°.
The modulus of elasticity is approx. 191,000 MPa at approx. 20 C° temperature.
In the quenched state, the material 1.3813 has a magnetic permeability of <= 1.01 G/Oe
In the cold-worked condition, material 1.3813 has a magnetic permeability of <= 1.03 G/Oe
In the hot worked condition, material 1.3813 has a magnetic permeability of <= 1.01 G/Oe
Sie haben Fragen zum Werkstoff oder möchten ihn bestellen? Füllen Sie kostenlos und unverbindlich unser Anfrageformular aus. Wir melden uns bei Ihnen für weitere Informationen.
Normen
| DIN / EN | US-Standard | AFNOR | UNI | JIS | istek |
|---|---|---|---|---|---|
| X40MnCrN19 | istek |
Werkstoffgruppe: Non-magnetizable steel
Isıl İşlem
Hot forming at approx. 850 - 1050 C°.
Solution annealing at approx. 1000 - 1050 C° , cooling water / air
Kimyasal Bileşim
| C % | Si % | Mn % | P % | S % | Cr % | N % |
| 0,30 - 0,50 | max 0,80 | 17,00 - 19,00 | max 0,100 | max 0,030 | 3,00 - 5,00 | 0,080 - 0,120 |
Mekanik Özellikler
| abgeschreckt | 0,2% Dehngrenze (Rp0,2) | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Kerbschlagarbeit (DVM) |
| >= 295 N/mm² | 740 - 930 N/mm² | >= 45 % | >= 124 Joule |
| kaltverformt | 0,2% Dehngrenze (Rp0,2) | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Kerbschlagarbeit (DVM) |
| >= 490 N/mm² | 830 - 1.030 N/mm² | >= 35 % | >= 103 Joule |
| warmkaltverformt | 0,2% Dehngrenze (Rp0,2) | Zugfestigkeit (Rm) | Bruchdehnung (A5, 65) | Kerbschlagarbeit (DVM) |
| >= 390 N/mm² | 830 - 1.030 N/mm² | >= 40 % | >= 124 Joule |